S355J2W+N / Corten Steel Plates
Weathering structural plate. Copper, chromium and nickel additions let a dense, adherent oxide patina form that seals the surface, so the structure can be left unpainted and the maintenance coating cycle disappears.
- Self-protecting patina removes the painting cycle
- Same 355 MPa yield and -20 C toughness as S355J2+N
- Supplied in the normalised condition for weld consistency
- Profile cut to architectural drawings
Available forms & sizes
| Form | Size range |
|---|---|
| Plates | 5 - 200 mm thk, up to 3000 mm wide, cut to size |
| Sheets & Coils | 2 - 12 mm thk, 1250 / 1500 / 2000 mm wide |
Chemical composition (%)
| Element | Min | Max |
|---|---|---|
| C | - | 0.16 |
| Cu | 0.25 | 0.55 |
| Cr | 0.40 | 0.80 |
| Ni | - | 0.65 |
| Mn | 0.50 | 1.50 |
Mechanical properties
| Property | Value | Unit |
|---|---|---|
| Yield Strength | 355 min (t <= 16 mm) | MPa |
| Tensile Strength | 470 - 630 | MPa |
| Elongation | 20 min | % |
| Impact Energy | 27 J min at -20 C | J |
Physical properties
| Property | Value | Unit |
|---|---|---|
| Density | 7.85 | g/cm3 |
| Modulus of Elasticity | 210 | GPa |
Typical applications
Frequently asked
[ 02 ] Other grades in Carbon Steel Plates
S355J2+N Steel Plates
Ex-stock DubaiNormalised structural plate with guaranteed 27 J impact energy at -20 C. The J2+N condition gives consistent toughness and flatness through thick sections, which is why it is specified for welded structures, crane and bridge work and heavy fabrication in the Gulf.
SA516 Grade 60 Plates
Mill indentCarbon pressure vessel plate for moderate and lower temperature service. The lower carbon of Grade 60 gives better formability and weldability than Grade 70, which suits cold-formed heads, thin shells and plant where notch toughness matters more than tensile strength.
SA516 Grade 70 Plates
Ex-stock DubaiThe default carbon pressure vessel plate. Grade 70 carries the highest tensile of the SA516 family, and for sour service it is supplied with controlled sulphur, calcium treatment and HIC / SSC testing so wet H2S equipment can be built from a qualified plate rather than an upgrade alloy.