Cupro Nickel 90/10 Seamless Pipes
The default seawater alloy. 90% copper with 10% nickel and a controlled iron addition builds a protective cuprous oxide film in seawater, and the inherent copper toxicity stops macrofouling — barnacles and mussels do not settle, so cooling lines stay clean without chlorination. Specified for ship and platform seawater systems, firewater ring mains and condenser tubing where the velocity stays below about 3.5 m/s.
- Protective oxide film gives long life in flowing seawater
- Natural biofouling resistance — no barnacle or mussel settlement
- Immune to chloride stress corrosion cracking
- Easy to weld and form, no post-weld heat treatment required
- Navy, DNV and Lloyd's approved supply available
الأشكال والمقاسات المتوفرة
| الشكل | نطاق المقاسات |
|---|---|
| الأنابيب غير الملحومة و الأنابيب | 1/8" - 12" NB seamless, 6 - 108 mm OD tube, 0.8 - 6 mm wall |
| الأنابيب الملحومة | 4" - 36" OD welded pipe to ASTM B467 |
| الألواح | 3 - 50 mm thk condenser plate and tube sheet (ASTM B171) |
| الصفائح واللفات | 0.6 - 3 mm thk sheet and coil |
| الفلنجات | 1/2" - 24", 150# - 300#, slip-on and weld neck |
| الوصلات | 1/2" - 24" butt weld elbows, tees, reducers and stub ends |
| القضبان الدائرية | 10 - 200 mm dia rod and bar |
التركيب الكيميائي (%)
| العنصر | الحد الأدنى | الحد الأقصى |
|---|---|---|
| Cu | Remainder | - |
| Ni | 9.0 | 11.0 |
| Fe | 1.0 | 1.8 |
| Mn | 0.5 | 1.0 |
| Pb | - | 0.02 |
الخصائص الميكانيكية
| الخاصية | القيمة | الوحدة |
|---|---|---|
| Yield Strength (0.2%) | 105 min (annealed) | MPa |
| Tensile Strength | 275 min (annealed) | MPa |
| Elongation | 30 min | % |
| Hardness | 60 - 90 | HV |
الخصائص الفيزيائية
| الخاصية | القيمة | الوحدة |
|---|---|---|
| Density | 8.94 | g/cm3 |
| Thermal Conductivity | 40 - 50 | W/m.K |
| Max Service Temperature | 300 | C |
| Max seawater velocity | 3.0 - 3.5 | m/s |
التطبيقات النموذجية
أسئلة متكررة
[ 02 ] درجات أخرى في Cupro Nickel
Cupro Nickel 70/30 Seamless Pipes
Mill indentThe higher-duty cupro nickel. Tripling the nickel to 30% raises strength, erosion-corrosion resistance and the allowable seawater velocity to around 4.5 m/s, and lifts the service temperature well above 90/10. It is the grade for pump and valve-adjacent piping, hot brine and MSF desalination heat recovery, and any line where turbulence or sand loading would strip the film off 90/10.
Cupro Nickel 66/30/2/2 (C71640)
Project supplyThe desalination variant of 70/30. Raising iron and manganese to about 2% each stabilises the protective film under high velocity, sand-laden and partly deaerated brine, which is exactly the duty inside MSF evaporator heat recovery and reject sections. Where 70/30 tubes thin at the inlet ends, C71640 holds.